PROPERTY |
TEST METHOD |
TEST CONDITION |
UNIT |
DATA |
Melt flow index |
ASTM D1238 |
200 oC, 5 kg220 oC, 10 kg |
g/10 ming/10 min |
4.5 |
Izod notched impact |
ASTM D256 |
1/8" at 23 o C 1/8" at 73.4 o F |
kg-cm/cm
ft-lb/in |
18.5 3.4
|
Tensile strength |
ASTM D638 |
23 o C 73.4 o F |
kg/cm 2 psi x10 3 |
430 6.12
|
Flexural strength |
ASTM D790 |
23 o C 73.4 o F |
kg/cm 2 psi x10 3 |
610 8.68
|
Flexural modulus |
ASTM D790 |
23 o C 73.4 o F |
x10 4 kg/cm 2 psi x10 5 |
2.20 3.13
|
Rockwell hardness |
ASTM D785 |
1/4" at 23 o C |
R-scale |
105 |
Heat distortion temperature |
ASTM D648 ASTM D648 |
1/4" at 18.6 kg/cm 2 1/4" at 264 psi 1/4" at 4.6 kg/cm 2 1/4" at 65.4 psi |
o C o F o C o F |
75 167
84 183 |
Flammability |
UL-94 |
HB at 3.2 mmV-O at 1.6 mm |
|
V-O |
|
|
|
|
FEATURES |
APPLICATIONS |
Flame retardant grade |
Pluck, electrical parts |
|
|
|
|
Remark: The values presented on the above are typical laboratory average and to be used as an approximate guideline and subject to change without notice. |
|